Svojstva, proizvodnja i primjena vermikularnog lijeva

završni rad

• Naslov (engleski): Properties, production and application of compacted graphite iron
• Autor: Zvonimir Petrović
• Mentor: Zoran Glavaš (mentor)
• Član povjerenstva: Stjepan Kožuh (predsjednik povjerenstva)
• Član povjerenstva: Zoran Glavaš (član povjerenstva)
• Član povjerenstva: Martina Lovrenić-Jugović (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Metalurški fakultet; Sisak
• Datum i država obrane: 2018-09-24, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Metalurgija

Sažetak

Vermikularni lijev je vrsta željeznog lijeva u kojem je većina ugljika prisutna u obliku vermikularnih grafitnih čestica. Te čestice nalaze se u metalnoj osnovi koja se uglavnom sastoji od ferita, ferita i perlita ili perlita. Po svojim fizikalnim i mehaničkim svojstvima može se svrstati između sivog i nodularnog lijeva.
Proizvodnja vermikularnog lijeva je znatno teža od proizvodnje sivog i nodularnog lijeva jer brojni procesni parametri utječu na stvaranje vermikularnog grafita tijekom skrućivanja. Već vrlo mala odstupanja od njihovih optimalnih vrijednosti mogu rezultirati stvaranjem listićavog ili nodularnog grafita.
Vermikularni lijev odavno je poznat. Međutim, otežani postupak proizvodnje ograničio je njegovu značajniju primjenu u prošlosti. Proširenje spoznaja o vermikularnom lijevu, napredak ljevačke tehnologije i kontrole procesa proizvodnje omogućili su njegovu širu primjenu. Danas se vermikularni lijev primjenjuje za brojne aplikacije. Najširu primjenu ima u industriji motornih vozila za komponente od kojih se istovremeno zahtijeva otpornost na toplinska opterećenja i čvrstoća.
U ovom preglednom radu prikazane su norme za vermikularni lijev, faktori koji utječu na njegova svojstva, proizvodnja vermikularnog lijeva te njegova svojstva i primjena.

Sažetak (engleski)

Compacted (vermicular) graphite iron is a type of cast iron in which the majority of the carbon is present in the form of compacted graphite particles. These particles are placed in a metal matrix which consists mainly of ferrite, ferrite and pearlite, or pearlite. According to its physical and mechanical properties, compacted graphite iron can be placed between gray and ductile iron.
Production of compacted graphite iron is more complicated than the production of gray and ductile iron because numerous process parameters influencing the formation of compacted graphite during solidification. Already very small deviations from their optimal values may result in the formation of flake or nodular graphite.
Compacted graphite iron has long been known. However, the difficult process of production has limited its significant application in the past. Increase of knowledge about compacted graphite iron, progress of foundry technology and production process control has enabled its wider application. Today, compacted graphite iron is used for numerous applications. It is mainly used in in the motor vehicle industry for components which at the same time must have a resistance to thermal loads and strength.
This review paper shows the standard for compacted graphite iron, the factors that affect its properties, production of compacted graphite iron and its properties and application.

• Ključne riječi: željezni ljevovi; vermikularni lijev
• Ključne riječi (engleski): cast irons; compacted (vermicular) graphite iron
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:115:484725
• Studijski program: Naziv: Metalurgija; smjerovi: Metalurško inženjerstvo, Industrijska ekologija; Smjer: Metalurško inženjerstvo; Vrsta studija: sveučilišni; Stupanj studija: preddiplomski; Akademski / stručni naziv: sveučilišni/a prvostupnik/ prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka metalurgije (univ. bacc. ing. met.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Repozitorij: Repozitorij Metalurškog fakulteta Sveučilišta u Zagrebu
• Datum i vrijeme pohrane: 2018-09-28 09:07:57